Investigating the effectiveness of phosphonate additives in hindering the calcium sulfate dihydrate scale formation

Authors

Rabizadeh,  Taher
External Organizations;

Peacock,  Caroline L.
External Organizations;

/persons/resource/benning

Benning,  Liane G.
3.5 Interface Geochemistry, 3.0 Geochemistry, Departments, GFZ Publication Database, Deutsches GeoForschungsZentrum;

External Ressource
No external resources are shared
Fulltext (public)
There are no public fulltexts stored in GFZpublic
Supplementary Material (public)
There is no public supplementary material available
Citation

Rabizadeh, T., Peacock, C. L., Benning, L. G. (2020): Investigating the effectiveness of phosphonate additives in hindering the calcium sulfate dihydrate scale formation. - Industrial and Engineering Chemistry Research, 59, 33, 14970-14980.
https://doi.org/10.1021/acs.iecr.0c03600


Cite as: https://gfzpublic.gfz-potsdam.de/pubman/item/item_5002768
Abstract
The effects of 20 ppm 1-Hydroxy Ethylidene-1,1-Diphosphonic Acid (HEDP), Amino Trimethylene Phosphonic Acid (ATMP), Polyamino Polyether Methylene Phosphonic Acid (PAPEMP), Diethylene Triamine Penta (Methylene Phosphonic Acid) (DTPMPA) and Bis(HexaMethylene Triamine Penta (Methylene Phosphonic Acid)) (BHMTPMPA) on the room temperature crystallization of calcium sulfate dihydrate (gypsum) were investigated by by in situ UV-Vis, XRD, XPS, ICP-OES, and SEM. Comparison between the additive-containing and additive-free experiments showed that BHMTPMPA was the most efficient antiscalant by completely inhibiting crystallization. Due to the chain length of the BHMTPMPA molecule, the crystallization kinetics decreased to a larger extent than DTPMPA. The increase in pH of the solution from ~ 4 to ~ 7, positively enhanced the efficiency of the phosphonates in inhibiting crystallization. Our results revealed that partially deprotonated phosphonate additives were strongly associated with gypsum crystals and / or potentially taken up into the crystal matrix resulted in a sudden and sharp increase in turbidity plots. Furthermore, phosphonate additives altered the thin, twinned gypsum crystals into thick needles.