Characterization of CO2 Pipeline Material from the Ketzin Pilot Site

Urheber*innen

Todorovic,  Jelena
External Organizations;

Torsæter,  Malin
External Organizations;

Opedal,  Nils
External Organizations;

/persons/resource/wiese

Wiese,  B.
CGS Centre for Geological Storage, Geoengineering Centres, GFZ Publication Database, Deutsches GeoForschungsZentrum;

/persons/resource/martens

Martens,  S.
CGS Centre for Geological Storage, Geoengineering Centres, GFZ Publication Database, Deutsches GeoForschungsZentrum;

Externe Ressourcen
Es sind keine externen Ressourcen hinterlegt
Volltexte (frei zugänglich)

838921.pdf
(Verlagsversion), 5MB

Ergänzendes Material (frei zugänglich)
Es sind keine frei zugänglichen Ergänzenden Materialien verfügbar
Zitation

Todorovic, J., Torsæter, M., Opedal, N., Wiese, B., Martens, S. (2014): Characterization of CO2 Pipeline Material from the Ketzin Pilot Site. - Energy Procedia, 63, 2610-2621.
https://doi.org/10.1016/j.egypro.2014.11.283


Zitierlink: https://gfzpublic.gfz-potsdam.de/pubman/item/item_838921
Zusammenfassung
Due to lack of relevant field data it is difficult to predict with sufficient accuracy the corrosion rates and CO2 flow in pipelines. Laboratory experiments are usually of short duration at small scales, failing to reproduce events such as repeated shutdowns. It is therefore important to learn from CO2 storage pilot sites, and the present paper reports characterization of stainless steel pipeline material from Ketzin. It was exposed to CO2 flow for about five years, including several shut-ins, and samples were collected from straight and bent sections with different proximity to heaters of the injection facility. The samples displayed no visual signs of severe corrosion, but were investigated in detail using scanning electron microscopy and a profilometer. This revealed that prolonged CO2 flow had roughened the inner pipe surfaces and caused some intergranular and pitting corrosion, especially close to heaters and in bent pipe sections.